Item内 容
|
Test condition条件
|
Criteria达到要求
|
1
|
End of charge voltage充电截止电压
|
4.28±0.05V
|
|
2
|
End of discharge voltage放电终止电压
|
2.5±0.1V
|
|
3
|
Standard charge model
标准充电模式
|
With charging voltage 4.2V, current .0.5C. continued to charge the battery pack, when charging current drops to 0.01C. charging is terminated, shall be full charged.
以0.5C电流恒流充电至4.2V,转4.2V恒压充电,直到充电电流≤0.01C电流
|
Charging time≤8h
充电时间≤8小时
|
4
|
Standard discharge Model
标准放电性能
|
After standard charging, waiting 1h, and discharging cell with 0.2C to3.0V;
以标准充电模式满充后,搁置1小时,以0.2C电流恒流放电至3.0V。
|
Discharge time ≥ 290min
放电时间≥290Min
|
5
|
1C discharge
1倍率放电性能
|
After standard charging, waiting 1h, and discharging cell with 1C current to3.0V;
以标准充电模式满充后,搁置1小时,以1C电流恒流放电至3.0V。
|
Discharge time ≥51Min
放电时间≥51Min
|
6
|
High temperature performance
高温性能
|
After fully charging, storage cell 2h at 55℃±2℃, and discharge cell to 3.0V with 1C.
电池满充后在55℃±2℃度的环境下搁置2小时,然后以1C电流放电至3.0V。
|
Discharge time ≥51Min;No visible distortion, fire or explosion,
放电时间≥51Min,电池外观无变形、无爆裂。
|
7
|
Low temperature performance
低温性能
|
After standard charging, storing cell in low temperature(-10±2)℃chamber at least 16~24h, then discharge cell to 3.0V with 0.2C.
以标准模式充电,将电池放入(-10±2)℃的低温箱中恒温16~24h后,0.2C电流恒流放电至3.0V。
|
Discharge time ≥210Min, No visible distortion, fire or explosion,
放电时间≥210Min,电池外观无变形、无爆裂。
|
8
|
Retention Capability
荷电保持能力
|
After full charging, storing the battery 28 days with 20°C ± 5°C condition, and then discharge with discharge current of 0.2C5A till 3.0V cut-off voltage, discharge time should be≥255min
电池满充电后,在20±5℃的环境条件下存放28天,然后以0.2C电流连续放电至3.0V终止电压,放电时间≥255min
|
Discharge time≥ 255min;
放电时间≥255Min
|
9
|
Cycle life
循环寿命
|
At 20±5℃ conditions, with discharge current of 0.5 C till 3.0V; Again with 0.5C constant current charging to 4.2V, then with constant voltage 4.2V charge until the charge current drops to 0.02 C, rest 30 min, with discharge current of 0.5 C till 3.0 V, rest 30 min, afte 300 cycles, the capacity with 0.2C discharge current should be≥ 80%
在20±5℃条件下以0.5C电流恒流放电至3.0V,再以0.5C电流恒流充电至4.2V,然后恒压4.2V充电至电流小于0.02C,搁置30min,以0.5C电流恒流放电至3.0V,放电结束后,搁置30min,重复循环300次后,0.2C电流放电容量应≥80%.
|
Cycle time≥ 300;循环次数≥300次
|